To control degradation rate of biodegradable poly(lactide)s (PLA), the stereochemical PLAs with different ratios of d-lactide and l-lactide units were synthesized by the ring open polymerization and a degradation behavior was measured by a Langmuir film balance. Degradation rates of mixture monolayers on alkaline subphase were investigated as a function of optical purity of mixture component, 100, 99, 97 and 95%. As increasing their optical purity, melting temperatures of mixtures from stereocomplexation increased. The degradation rate of mixture monolayer with 100% optical purity was much slower than that of each homopolymer one and the others showed 2 step degradation behaviors. In the first step, the degradation which is faster than that of each homopolymer occurs in the uncomplexed region, and secondly, the degradation occurred in the complexed region which showed similar degradation rate to that of 100% optical purity. These results indicate that the alkaline degradation of stereochemical PLAs could be controlled by stereochemistry and stereocomplexation between enantiomer PLAs.